Assessing Microstructural and Mechanical Characteristics of Ni/Az91 Composites Manufactured Using Hot Pressing Technique for Automotive Applications
(Elsevier Science Sa, 2025) Kelen, Fevzi
In the present study, AZ91 magnesium alloy matrix composite materials reinforced with nickel microparticles in different volumetric ratios were successfully manufactured via hot pressing technique. The density values, morphological properties, and room and high-temperature mechanical characteristics of the produced materials were analyzed in detail. In the composite specimens, it was determined that the density values increased linearly with the increase in reinforcement content, and that the actual density values were very close to the theoretical density values. The porosity was detected to be 2.74 % in the composite material containing the maximum amount of reinforcement. It was observed that nickel microparticles did not cause a significant change in the grain size of the matrix alloy at the micrometer-scale after hot pressing. In the microstructural analyses, the alpha-Mg, (3-Mg17Al12, gamma-Ni, and Mg2Ni phases were identified. Apart from these phases, no other phases were encountered in the morphological analysis. A good interface has been achieved between the matrix and the reinforcement phases, which is crucial for mechanical behavior. In mechanical tests conducted at different temperatures, it was found that the nickel reinforcement material significantly improved the compressive yield strength and compressive strength of the composite materials by 20 % and 69 %, respectively, at room temperature. In terms of elongation, it has resulted in a significant increase of 91 % compared to matrix alloy materials. The final characteristics of the composite materials are assessed to possess considerable potential for application in various fields, particularly in the automotive industry, where energy efficiency and low density are critical.
Az91 Magnezyum Matrisli Kompozit Malzemelerin Korozyon Özelliklerinin Araştırılması
(2022) Aydoğmuş, Tarık; Gavgalı, Mehmet; Kelen, Fevzi
TiNi mikro partiküller ile %5-25 hacimsel oranlarda takviye edilen AZ91 magnezyum matrisli kompozit malzemelerin korozyon özellikleri %3.5 NaCl çözeltisi içerisinde potansiyodinamik polarizasyon (PDS) yöntemi ile araştırılmıştır. Elektrokimyasal değerlendirmeler Tafel ekstrapolasyonu tekniği ile saptanmıştır. Metalografik incelemeler taramalı elektron mikroskobu (SEM) ve optik mikroskop (OM) kullanılarak gerçekleştirilmiştir. Mikroyapısal analizler elektrokimyasal değerler ile birbirini desteklemektedir. Korozyon potansiyeli $(E_{corr})$ ve korozyon akım yoğunluğu (ίcorr) değerlerinin artan takviye miktarıyla artığı belirlenmiştir. Korozyon sonrası yüzey incelemelerinde tüm kompozit numunelerde çukurcuk korozyonu gözlenmiştir. Matris fazda yer alan alan β-Mg17Al12 intermatalik çökeltilerin ve yüzey morfolojisindeki homojensizliklerin kompozit malzemelerin korozyon dayanımı üzerinde önemli bir etkiye sahip olduğu tespit edilmiştir.
Effect of Aluminum Addition on the Microstructural and Mechanical Properties of Mg Pumice Composites
(2023) Timur, Demet Sevin; Aydoğmuş, Tarık; Kelen, Fevzi
Yapacağımız çalışmadaki temel amacımız toz metalürjisi yöntemi ile daha ucuz, hafif ve dayanıklı kompozit malzeme elde etme amacı ile alüminyum ilavesi pomza takviyeli magnezyum matrisli kompozit malzeme üretilmesidir. Yapılacak olan bu tez çalışmasının asıl amacı magnezyum ile pomza içerisinde bulunan SiO2'nin reaksiyona girmesini sağlayıp in-sitü yöntemiyle Mg2Si ve MgO takviyeli magnezyum matrisli kompozit malzemeler elde etmektir. Buna bağlı olarak ilave edeceğimiz alüminyum ise çekme mukavemetini ve sertliğini arttıracaktır. Katı eriyik sertleşmesi ve çökelme sertleşmesi (Mg17Al12) mekanizmaları ile düşük sıcaklıkta alaşımın mukavemetine katkıda bulunacaktır. DSC analizi ile magnezyum ve pomzanın reaksiyona girme sıcaklığı ölçüldükten sonra sıcak pres için numune hazırlanacaktır. Önceden belli olan sıcaklık ve basınçta pres işlemi gerçekleştirilecektir. sıcak pres işleminden sonra üretilen kompozitlerin yoğunluk(arşimet yöntemi), içyapıdaki tane boyutları (xrd, sem analizleri), mekanik (basma deneyleri, mikrosertlik) özellikleri belirlenecektir.
Effect of Magnesium Addition on Aluminum Pumice Composites
(2023) Anaran, Gülsüm; Aydoğmuş, Tarık; Kelen, Fevzi
Yapılan bu çalışma kapsamında toz metalürjisi yöntemini kullanarak Al matrisli pomza takviyeli ve Mg alaşım elementli kompozit malzemeler üretilmiştir. Bu çalışmanın esas amacı Al matrisli pomza takviyeli kompozit malzemelerine Mg ilavesinin etkisini incelemek ve Mg ile pomza içerisindeki SiO2'nin tepkimeye girmesini sağlayıp in-sitü yapıdaki Mg2Si ve MgO fazların oluşmasını sağlamaktır. Kompozit malzemeler sıcak presleme yöntemi ile üretilmiş olup sıcak presleme süresi 1 saat, sıcaklık 600 °C olarak optimize edilmiştir. Deneysel çalışmaların sonucu üretilen kompozit malzemelerin XRD ve SEM çalışmaları ile mikroyapı özellikleri elde edilmiştir. Kompozit numunelerin mekanik özelliklerinin tespiti için basma testleri yapılmıştır. Ayrıca 4x4x6 mm boyutlarında tel erezyon metodu ile kesilen numunelerin yoğunluk ve gözeneklilik değerleri Arşimet metodu ile belirlenmiştir. Elde edilen sonuçlara göre üretimi gerçekleştirilmiş olan kompozitlerin, içyapılarında Mg2Si, MgO, Saf Si, Al3Mg2 ve MgAl2O4 fazları oluşmuş takviye malzemesinin matris içerisinde homojen olarak dağıldığı gözlemlenmiştir. Yapılan basma testi sonucunda Mg ilavesi ile birlikte basma mukavemeti % 9 Mg' a kadar artmış sonrasında azalma göstermiştir. Akma dayanımı ise farklı oranlarda Mg ilavesi için sabit kalmıştır. Diğer taraftan kırılma birim şekil değişimi artan Mg içeriğiyle azalma göstermiştir.
Fabrication, Microstructure and Mechanical Properties of Novel Titanium and Nickel Micro-Particulates Reinforced Az91d Magnesium Alloy Metal Matrix Hybrid Composites
(Elsevier Science Sa, 2023) Kelen, Fevzi
In the present study, AZ91D magnesium alloy has been successfully produced for the first time by reinforcing with a combination of Ti and Ni microparticles. The manufacture of hybrid composites reinforced with elemental powders at the volumetric proportions of 0-25 % was conducted using the powder metallurgy technique. As a result of optimized fabrication parameters, in all the specimens were nearly obtained full density and a pore-free microstructure. During the morphological examinations were detected alpha-Mg, beta-Mg17Al12, Ti and Ni phases, apart from these, no unwanted secondary phases such as oxide, carbide and nitride were founded. A clean interface formation was observed between the matrix and reinforcement phases in which no chemical reaction occurs. The combined use as reinforcement material of Ti and Ni elements for the first time resulted in approximate ratios of 29 %, 80 % and 30 % significant enhancement in the yield strength, compressive strength and ductility values of the matrix alloy, respectively. Hybrid specimens were determined to have better mechanical properties than those of the unreinforcement matrix alloy at all test temperatures. Produced hybrid composites have been established to be enough to easily meet the temperatures and stresses that automobile components are exposed to under service conditions. In addition, their low-density values of 2.048-3.011 g/cm3 show to compose a significant alternative to conventional materials like iron, steel and even aluminum which are often used in the generation of automobile parts.
Improving Helicoid Type Filter With Water Flow for Vacuum Cleaner
(2009) Kelen, Fevzi; Yumak, Hasan
Vakumlu elektrikli süpürgeler çok ince tozları da hava ile karışık olarak emmektedir. Günümüzde bu süpürgelerde farklı tipte kuru ve sulu tip filtreler kullanılmaktadır. Bunlarda en yaygın olarak bilinen kâğıttan veya elyaf içeren malzemelerden yapılmış olan kuru toz filtreleridir. Ancak bu filtrelerin toz partiküllerini tutmadaki verimleri oldukça düşüktür. Ortamdaki toz, içerisinde mite, polen, küf, kimyasal bileşikler ve birçok mikroorganizma bulundurur. Bunlar hem sağlık açısından hem de ortamdaki eşyalar açısından zararlıdır. Son yıllarda vakumlu elektrikli süpürgeler için geliştirilmiş sulu tip filtrelerde, kullanımdaki zorluklar, toz partiküllerini tutmadaki verim düşüklüğü ve maliyetlerinin yüksek oluşu bunların dezavantajları olarak göze çarpmaktadır.Bu çalışmada elektrikli süpürgelerde kullanılmak üzere helezonik tip su yıkamalı bir hava filtresi prototipi tasarlanmıştır. Tasarlanan prototip, suyun küçük çaptaki partikülleri yakalamadaki üstün özelliğinden ve santrifüj ayırma esasından faydalanılarak geliştirilmiş olup, iki kısımdan oluşmaktadır. Tasarlanan prototip ile bir seri deney gerçekleştirilmiş, bu deneylerde toz materyali olarak portland çimento ve bentonit kullanılmıştır. Deneylerde filtre etkinliği % 82.1 - % 96 arasında, filtre direnci ise 8-12 mmHg değerleri arasında bulunmuştur. Yapılan deneysel çalışmalar sonucu elde edilen veriler, tasarlanan prototip ünitenin, filtre etkinliği, çalışma performansı ve diğer işletme koşulları açısından başarılı olduğunu ortaya koymuştur.Anahtar Kelimeler: Helezonik su yıkamalı filtre, Toz filtresi, Filtre etkinliği, Elektrikli süpürge.
Magnezyum ve Alaşımlarının Otomotiv Endüstrisindeki Önemi ve Uygulamaları
(2021) Kelen, Fevzi
Dünya petrol rezervlerinin hızla tükenmesi, artan yakıt ekonomisi talepleri ve egzoz emisyon değerlerine getirilen yasal sınırlamalar otomotiv endüstrisini modern hafif yapılara yönlendirmiştir. Otomobillerde kütle azaltımı ile hem yakıt verimliliğinin sağlanması hem de yanma sonucu açığa çıkan zararlı egzoz emisyonlarının en aza indirgenmesi hedeflenmiştir. Bu bağlamda üstün özelliklere sahip malzemelere ihtiyaç duyulmuştur. Magnezyum ve alaşımları düşük yoğunluk, yüksek özgül dayanım, kolay geri kazanım ve mükemmel sönümleme kapasitesi gibi karakteristik özellikleri ile otomotiv uygulamaları için en dikkat çekici yapısal malzemeler olarak ön plana çıkmaktadır. Bu malzemeler otomobillerin iç donanım, karoseri, şasi, güç aktarma organları ve araç ön alanı gibi temel sistem ve bileşenlerinde kullanılarak ağırlıkta önemli bir kazanım sağlayabilir. Böylece gerek yakıt sarfiyatı gerekse de insan sağlığı ve çevre kalitesi açısından ciddi tehdit unsuru oluşturan egzoz emisyonları minimize edilebilir. Bu çalışmada, magnezyum ve alaşımlarının otomotiv endüstrisindeki önemine, mevcut ve olası uygulamalarına dikkat çekilmek istenmiştir.
Magnezyum ve Magnezyum Esaslı Malzemelerde Korozyon
(2023) Kelen, Fevzi
Düşük yoğunluk, yüksek spesifik mukavemet, kolay geri kazanım ve mükemmel sönümleme kapasitesi gibi karakteristikleri ile modern hafif araçlar için en dikkat çekici yapısal malzemeler olarak ön plana çıkan magnezyum ve magnezyum esaslı malzemeler otomotiv ve havacılık gibi ulaşım dalları için önemli bir potansiyel oluşturmaktadır. Yakıt verimliliğinin arttırılması ve karbondioksit salınımının en aza indirgenmesinin amaçlandığı bu alanlarda direksiyon simidi, gösterge paneli, torpido kapağı ve karter gibi birçok uygulamaları bulunmaktadır. Bilhassa otomotiv endüstrisinde tüketim hacimleri her geçen gün artmaktadır. Fakat düşük korozyon dayanımları kullanımlarını gerek otomotiv sektöründe gerekse de endüstride demir, çelik ve alüminyuma kıyasla önemli oranda kısıtlamaktadır. Bu bağlamda yüksek korozyon dayanımlı magnezyum esaslı malzemelerin geliştirilmesi başlıca beklenti haline gelmiştir. Bu çalışmada yakıt tasarrufu ve düşük emisyon bakımından en umut verici yapısal malzemeler olan magnezyum ve magnezyum esaslı malzemelerin korozyon özelliklerine ve korozyon dayanımlarının nasıl iyileştirilebileceğine dikkat çekilmek istenmiştir.
Microstructure and Mechanical Properties of a Novel Tini Particulate Reinforced Az91 Metal Matrix Composite
(Elsevier Science Bv, 2018) Kelen, Fevzi; Gavgali, Mehmet; Aydogmus, Tarik
A new AZ91/TiNi composite has been developed in the present study. The composite containing 20% (vol.) TiNi reinforcement micro-particles was produced by hot pressing of initial prealloyed AZ91D and Ti49.2Ni50.8 powders at 420 degrees C for 1 h. Microstructural analysis revealed that matrix and reinforcement phases did not react each other during processing and a good bonding which is free from porosity, oxide and carbides was attained. Ti49.2Ni50.8 reinforcement increased room temperature yield strength, compressive strength and ductility of AZ91D alloy 5%, 50% and 30%, respectively. Most importantly, yield strength of the composite at 100 degrees C was found to be 267 MPa, 50% higher than that of AZ91D alloy (176 MPa) due to stress-induced martensitic transformation observed in the reinforcing alloy. (C) 2018 Elsevier B.V. All rights reserved.
Nikel Partiküller ile Takviye Edilmiş Magnezyum Matrisli Kompozitlerin Üretimi ve Karakterizasyonu
(2023) Kelen, Fevzi
Metal matrisli kompozit malzemeler otomotiv endüstrisinde yaygın olarak kullanılmaktadır. Düşük ağırlığın son derece önemli olduğu bu alanda magnezyum esaslıların tüketim hacimleri her geçen gün artmaktadır. Fakat oda sıcaklığında gözlenen düşük süneklilikleri ve yetersiz dayanımları hem otomotiv sektöründe hem de endüstride demir, çelik ve alüminyuma göre kullanımlarını önemli oranda kısıtlamaktadır. Mevcut çalışmada, hacimce %0-%10 oranlarında, mükemmel süneklilik, iyi tokluk ve yüksek elastik modül gibi üstün özelliklere sahip nikel mikro partiküller ile takviye edilmiş magnezyum matrisli kompozit malzemeler toz metalürjisi yöntemlerinden tek eksenli sıcak presleme tekniği ile imal edilmiştir. Üretim parametrelerinin optimizasyonu sonucu tüm numunelerde yaklaşık olarak tam yoğunluğa ulaşılmış ve gözenek içermedikleri tespit edilmiştir. Mikroyapısal incelemelerde α (Mg) ve Ni fazlarına ilaveten Mg2Ni fazı da gözlenmiştir. Bu bileşik, ayrıca, XRD analizlerinde de belirlenmiştir. Güçlendirici ilavesi ile matris malzemesinin oda sıcaklığı akma ve basma dayanımlarında sırasıyla %37 ve %35 oranlarında iyileşmeler elde edilmiş ve tüm test sıcaklıklarında saf magnezyuma göre daha yüksek değerlere sahip olduğu görülmüştür. Kompozit malzemeler gerek mekanik özellikleri gerekse de düşük yoğunlukları ile otomotiv ve endüstride kullanılan geleneksel malzemelere önemli bir alternatif teşkil ettiği saptanmıştır.
Novel Magnesium Matrix Hybrid Composites Manufactured Through Powder Metallurgy Technique
(Elsevier, 2023) Kelen, Fevzi
In the present study, novel magnesium matrix hybrid composites have been developed through the addition of titanium and nickel micro particulates using the hot pressing technique which is one of the powder metallurgy methods. Titanium and nickel elements were first-time used in combination as reinforcing materials in the manufacture of hybrid composites. A clean interface was obtained free from porosity, oxide and unwanted secondary phases between the matrix and reinforcement in all produced samples. In addition to the matrix and reinforcement phases, the Mg2Ni phase was also observed in the microstructural characterizations. The existence of this phase was confirmed through XRD analyses, its peak intensity increased with the increasing amount of reinforcement. While the addition of Ti and Ni provided a mean of 33 % and 83 % improvement in the yield strength and compressive strength of pure magnesium at room temperature, respectively, they did not cause a serious decrease in ductility values compared to those of ceramic reinforcement materials. The yield and compressive strengths of hybrid composites were found to be greater than those of the reference sample at all test temperatures. The mechanical properties such as yield strength, compressive strength and ductility together with low densities have shown that produced hybrid materials constitute an important alternative to traditional materials such as iron, steel and even aluminum frequently used in the manufacture of automobile components.
Processing of Porous Β-Type Ti74nb26 Alloys for Biomedical Applications
(Elsevier Science Sa, 2021) Aydogmus, Tarik; Palani, Dana Kareem Hameed; Kelen, Fevzi
Ti74Nb26 alloys with porosities in the range of 45-68% were produced employing Mg space holder technique combined with hot pressing using elemental Ti, Nb and Mg powders. Powder mixtures were hot pressed at 600 degrees C (below the melting point of Mg, 650 degrees C) for 1 h under a constant pressure of 50 MPa and flowing argon gas. After hot pressing samples were sintered in a vertical furnace at 1200 degrees C (above the boiling temperature of Mg, 1090 degrees C) for 4 h under flowing inert argon gas atmosphere. Evaporation and removal of Mg particles from the samples were carried out during sintering simultaneously. X-ray diffraction and scanning electron microscopy analysis revealed that beta phase was the main phase in the microstructure of all the samples. A small amount of a and undissolved pure Nb were also observed. Room temperature Young's moduli and compressive strength of the specimens increased with decreasing porosity and were in the range of 1.6-14 GPa and 14-136 MPa, respectively. The mechanical properties of the 45%, 54% and 59% porous alloys were sufficient for both cortical and cancellous bone replacement applications. The alloy with a porosity content of 68% demonstrated mechanical properties suitable only for the cancellous bone implants. (C) 2021 Elsevier B.V. All rights reserved.
Sıcak Presleme ve Yüksek Sıcaklık Sinterleme Kombinasyonu İle Β Tipi Biyomedikal Ti74nb26 Alaşımının Üretimi
(2020) Aydoğmuş, Tarık; Kelen, Fevzi; Zangana, Nuaman
Ti-Nb alaşımları genellikle döküm yöntemi ile üretilirler. Saf Ti ve Nb’un erime sıcaklıkları oldukça yüksek olduğundan döküm yoluyla Ti-Nb alaşımlarını üretmek maliyetlidir. Toz metalurjisi yöntemi ile bu alaşımları çok daha düşük sıcaklıklarda (Ti erime sıcaklığından daha az) ve tamamen katı halde ekonomik olarak üretmek mümkündür. Bu çalışmada Ti74Nb26 alaşımları saf Ti ve saf Nb tozları kullanılarak, sıcak presleme ve yüksek sıcaklık sinterlemesinin ilk kez birlikte uygulanması ile üretilmiştir. Üretim sürecinde uygulanan işlem sıcaklığı ve zamanının yoğunluk, mikroyapı ve mekanik davranış üzerindeki etkileri araştırılmıştır. Yoğunluk ölçümleri, 800 °C'de yapılan sıcak presleme işleminin tam yoğunluğu sağladığını göstermiştir. XRD ve SEM incelemeleri, sinterleme süresinin artmasıyla birlikte β fazı oluşumunun arttığını ortaya koymuştur. Ana faz β'ya ilaveten, mikroyapıda az miktarda α fazı ve çok az miktarda saf Nb gözlenmiştir. Mekanik özellikler tek eksenli basma ve mikro Vickers sertlik testleri ile belirlenmiştir. Mekanik test sonuçları, 1200 °C'de 4 saatlik sinterlemenin en yüksek sertlik (336 HV), elastik modül (44 GPa), akma mukavemeti (894 MPa) ve basma mukavemeti (1178 MPa) değerlerini sağladığını göstermiştir.
Sıcak Presleme Yöntemi ile Az91 Magnezyum Alaşımının Üretimi
(2020) Aydemir, Erhan; Aydoğmuş, Tarık; Kelen, Fevzi
En çok kullanılan ticari magnezyum (Mg) alaşımı olan AZ91’in %90’ı basınçlı döküm yöntemiyle üretilmektedir.Basınçlı dökümün birçok avantajı olmasına rağmen, işlem sırasında oluşan gaz boşlukları nedeniyle bu yöntemleüretilen AZ91 alaşımlarına ısıl işlem uygulanamamakta ve kaynak sırasında çeşitli problemlerle karşılaşılmaktadır.Bu çalışmada, mikroyapısında üretim sonrasında herhangi bir şekilde hapsolmuş gaz ve boşluk içermeyen AZ91alaşımlarının üretilmesi hedeflenmiştir. Ön alaşımlı AZ91D tozları 420, 450 ve 500 °C sıcaklıklarında 1 saatsüreyle sıcak preslenerek numuneler üretilmiştir. Presleme basıncı 50 MPa olarak sabit tutulmuştur. Üretilennumuneler tel erezyon ile 5x5x10 (mm) boyutlarında kesildikten sonra Arşimet metodu ile yoğunlukları ölçülmüş,X-Işını Difraktometresi (XRD) ve Taramalı Elektron Mikroskobu (SEM) ile mikroyapıları incelenmiştir. 450 ve500 °C’de yapılan sıcak presleme işlemi sırasında AZ91 alaşımında kısmi erime meydana geldiği gözlenmiş vebunun nedeninin Mg-Al ikili faz diyagramındaki 437 °C’de yer alan ötektik faz dönüşümünün gerçekleşmesiolduğu ortaya konulmuştur. 420 °C’de 1 saat süre ile yapılan sıcak presleme sonrasında AZ91 alaşımının tamyoğunluğa ulaştığı tespit edilmiştir. XRD ve SEM analizleri sonucunda mikroyapının α (Mg’ca zengin) ve β(Mg17Al12) fazlarından oluştuğu belirlenmiştir. Üretilen alaşımların mekanik özellikleri oda sıcaklığı, 100, 150 ve200 °C’de yapılan basma testleri ile belirlenmiştir. Sıcak presleme yöntemiyle üretilen AZ91 alaşımının mekaniközelliklerinin döküm yöntemleriyle üretilenlerden daha iyi olduğu görülmüş, akma dayanımı, basma dayanımı vesüneklik için sırasıyla 183 MPa, 241 MPa ve %10.1 değerleri elde edilmiştir. Beklendiği üzere, test sıcaklığıarttıkça akma ve basma mukavemetlerinde azalma, süneklikte ise artış görülmüştür.
Tek Eksenli Sıcak Presleme Tekniği ile İmal Edilen Magnezyum Matrisli Kompozit Malzemelerin Korozyon Davranışlarının İncelenmesi
(2022) Aydoğmuş, Tarık; Gavgalı, Mehmet; Kelen, Fevzi
Mevcut çalışmada, tek eksenli sıcak presleme tekniği ile üretilen %5-%25 hacimsel oranlarda TiNi içeren magnezyum matrisli kompozit malzemelerin korozyon deneyleri potansiyodinamik polarizasyon (PDS) testleri ile %3.5 NaCl çözeltisi içerisinde gerçekleştirilmiştir. Kompozit numunelerin korozyon potansiyeli $(E_{cor})$ ve korozyon akım yoğunluğu $(ί_{corr})$ değerleri Tafel ekstrapolasyonu metodu ile belirlenmiştir. Metalografik incelemeler mikroyapıda gözlemlenen değişimlerin elektrokimyasal değerler ile tutarlı olduğunu göstermiştir. Potansiyodinamik polarizasyon analizlerinde güçlendirici içeriğine bağlı olarak korozyon potansiyeli değerlerinin yanı sıra korozyon akım yoğunluğu değerlerininde önemli oranlarda arttığı saptanmıştır. Korozyon sonrası morfolojik incelemelerde numune yüzeylerinde çukurcuk korozyonu ile birlikte kurtçuk korozyonu da gözlenmiştir.
Tini Particle-Reinforced Magnesium Matrix Composites: Production, Microstructure, Phase Transformations, and Mechanical Properties
(Wiley-v C H verlag Gmbh, 2025) Kelen, Fevzi; Gavgali, Mehmet; Aydogmus, Tarik
Magnesium matrix composites reinforced with 5-25 vol% Ti49.2Ni50.8 microparticles are produced by uniaxial hot pressing technique. Powder mixtures are hot pressed in cylindrical graphite dies under 50 MPa pressure for 1 h at 600 degrees C. Density measurements show that specimens reach almost full density and do not contain any pores. Microstructural analyses demonstrate that undesired secondary phases or compounds do not form at matrix/reinforcement interface. As a result of aging heat treatment performed simultaneously with the manufacturing process, martensite phase (B19 ') and Ti3Ni4 precipitates are also observed in the microstructure of reinforcing materials in addition to the main austenite (B2) phase. The room-temperature yield strength and compressive strength of the composite materials range between 60 and 86 MPa and 232 and 296 MPa, respectively. Although the ductility values decrease with increasing reinforcement content, the decrease is less than those of ceramic and other metallic reinforced composites. The ductility is determined to be 17.6% for the composite with the highest reinforcement content. In contrast to the reference and conventional materials, the yield strengths of the composite samples produced increase significantly with the increasing temperature up to 100 degrees C. This unusual behavior is attributed to the stress-induced martensitic transformations observed in TiNi alloys.
Toz Metalürjisi Yöntemi ile Üretilmiş Magnezyum Matrisli Kompozitlerin Korozyon Duyarlılıkları
(2019) Aydoğmuş, Tarık; Kelen, Fevzi; Gavgalı, Mehmet; Dikici, Burak
Bu çalışmada, hacimce %5-25 oranında TiNi mikro partikül içeren magnezyum matrisli kompozitlerin korozyondavranışları %3,5 NaCl çözeltisi içerisinde potansiyodinamik polarizasyon (PDS) testleri ile belirlenmiştir.Korozyon potansiyeli (Ecor) ve korozyon akım yoğunluğu (ίcorr) değerleri Tafel ekstrapolasyonu yöntemi ilesaptanmıştır. İçyapıdaki değişimler ve elektrokimyasal sonuçlar birbirini desteklemektedir. Kompozitmalzemelerde artan takviye oranı ile birlikte hem korozyon potansiyeli hem de korozyon akım yoğunluğudeğerlerinin artığı gözlenmiştir. Korozyon testlerinden sonra gerçekleştirilen morfolojik incelemelerde yüzeydeçukurcukların yanı sıra kurtçuklar da tespit edilmiştir.